Effect of Molybdate on Corrosion Performance of Oxide Coating Produced on 7075 Al Alloy Using PEO
2022
In this research, plasma electrolytic oxidation (PEO) coatings were prepared on 7075 Al alloy in a silicate-based solution with Na2MoO4 additive using a unipolar waveform at constant current density. The coatings displayed micro-pores, micro-cracks, pancake-like and crater-like features, and also solidified molten oxide particles on the surface. The coatings were majorly composed of Al2O3 (γ, δ, and α), SiO2 (amorphous), and MoO3 phases, which confirms the incorporation of molybdenum in the case of additive-containing coatings. Molybdenum species were transported through cracks, channels, and micropores, as the ready access pathways into the coating and partly sealed the c…
Synergistic effect of W incorporation and pulsed current mode on wear and tribocorrosion resistance of coatings grown by plasma electrolytic oxidatio…
2019
Ceramic coatings were grown by plasma electrolytic oxidation on 7075 Al alloy using unipolar and bipolar pulsed current waveforms with 20 and 40% cathodic duty cycles, from a silicate-based bath without and with the addition of Na2WO4. Pancake-like morphology was dominant on the coatings grown by unipolar waveform, while the bipolar waveforms promoted volcano-like morphology, increased the roughness of the coating surface and the formation of more compact layers. The coatings produced using the bipolar waveforms provided higher resistances toward both tribocorrosion and dry sliding conditions, while further improvement was achieved by the presence of tungsten. The coatings produced in tungs…